Steel Products
- STEEL BILLET
- REBAR / DEBAR
- WIRE ROD
- HOT ROLLED COIL (HRC)
- COLD ROLLED COIL (CRC)
HEMATITE PIG IRON[also known as FOUNDRY PIG IRON] is used mainly in the manufacture of grey iron castings in cupola or induction furnaces
C | Si | Mn | P | S | |
L1 | 3.50-4.50 % | 3.20-3.60 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L2 | 3.50-4.50 % | 2.80-3.20 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L3 | 3.50-4.50 % | 2.40-2.80 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L4 | 3.50-4.50 % | 2.00-2.40 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L5 | 3.50-4.50 % | 1.60-2.00 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L6 | 3.50-4.50 % | 1.20-1.60 % | 0.40-0.80 % | 0.08 % max | 0.04 % max |
L5 – L6 Low Mn | 3.50-4.50 % | 1.00-2.00 % | 0.099 % max | 0.08 % max | 0.04 % max |
SIZE | 10-12 kg ingots without notches | ||||
PACKING | Bulk |
BASIC PIG IRON, used mainly in electric arc steelmaking
Basic Pig Iron | C | Si | Mn | P | S |
LowMn | 3.50-4.50 % | 1.20 % max | 0.099 % max | 0.08 % max | 0.05% max |
PL1 / PL2 | 3.50-4.50 % | 0.6-1.20 % | 0.40-0.80 % | 0.08 % max | 0.05% max |
SIZE | 10-18 kg ingots without notches | ||||
PACKING | Bulk |
NODULAR PIG IRON, used in the manufacture of ductile [also known as nodular or spheroidal graphite – SG] iron castings.
Nodular Pig Iron | C | Si | Mn | P | S |
NODULAR | 3.50-4.50 % | 1.0 % max | 0.05 % max | 0.05 % max | 0.015 % max |
NODULAR HP | 3.50-4.50 % | 1.0 % max | 0.04 % max | 0.04 % max | 0.010 % max |
SIZE | 10-12 kg ingots without notches | ||||
PACKING | Bulk |
Ferro Silicon is a universal “heat-blocker” used in the production of carbon and stainless steels. This additive is used with other ferro alloys in the deoxidising process of steel, as well as in the production of silicon itself. It is also used in the production of cast iron, as it can accelerate graphitisation. Ferro Silicon replaces the need for ferro manganese, spiegeleisen and calcium silicides in the manufacturing process.
Si | Al | C | P | S | |
FeSi 45 % | 45 % min | 2.00 % max | 0.20 % max | 0.03% max | 0.02 % max |
FeSi 65 % | 65 % min | 1.50 % max | 0.15 % max | 0.03% max | 0.02 % max |
FeSi 75 % | 75 % min | 1.50 % max | 0.15 % max | 0.03% max | 0.02 % max |
FeSi 75 % Low Al |
75 % min | 1.00 % max | 0.05 % max | 0.03% max | 0.02 % max |
FeSi 75 % High Purity |
75 % min | 0.10 % max | 0.03 % max | 0.03% max | 0.02 % max |
SIZE | 1-3 mm / 3-10 mm / 10-50 mm / 10-100 mm | ||||
PACKING | Bulk or 1 mt big-bag |
Ferro-manganese is used mainly in the steel industry for hardening and desulphurisation of steel and as a deoxidizer, making the slag more fluid.
Mn | C | Si | P | S | |
FeMn HC | 75 % min | 6-8 % | 1.50 % max | 0.25 % max | 0.03 % max |
FeMn HC Low P |
76/78 % min | 6-8 % | 1.50 % max | 0.10 % max | 0.03 % max |
FeMn MC | 80 % min | 1.50 % max | 1.50 % max | 0.20 % max | 0.03 % max |
FeMn LC | 80 % min | 0.50 % max | 0.50 % max | 0.025 % max | 0.03 % max |
SIZE | 1-3 mm / 3-10 mm / 10-50 mm / 10-100 mm | ||||
PACKING | Bulk or 1 mt big-bag |
Ferro Silico Manganese is used as a deoxidizer and an alloying element in steel. It can be used as a substitute for Ferro Silicon and Ferro Manganese when added to make different types of steel.
Mn | Si | C | P | S | |
FeSiMn 6014 | 60 % min | 14 % min | 2.0 % max | 0.30 % max | 0.05 % max |
FeSiMn 6517 | 65 % min | 17 % min | 2.0 % max | 0.30 % max | 0.03 % max |
FeSiMn 7018 | 70 % min | 17 % min | 2.0 % max | 0.30/0.50 % max | 0.03 % max |
SIZE | 10-50 mm / 10-80 mm | ||||
PACKING | Bulk or 1 mt big-bag |
Ferro Silicon Magnesium is one of the best nodularizers due to its low levels of magnesium oxide and high nodularization . This material is used to modify the graphite flakes in the iron making process.
Ferro Silico Magnesium | Mg | Si | Ca | TRE | La | Al |
FeSiMg | 5.50–6.50 % | 43.0–48.0 % | 0.80–1.20 % | 0.80–1.20 % | 0.40-0.80 % | |
FeSiMgMCa | 5.50–6.50 % | 43.0–48.0 % | 1.80–2.00 % | 0.80–1.20 % | 0.40-0.80 % | |
FeSiMgHMg | 8.00–10.00 % | 43.0–48.0 % | 0.80–1.20 % | 0.80–1.20 % | 0.40-0.80 % | |
FeSiMgLa | 5.50–6.50 % | 43.0–48.0 % | 0.80–1.20 % | 0.35–0.45 % | 0.40-0.80 % | |
SIZE | 1-10mm / 2-20 mm / 3-25 mm / 6-30 mm and as percustomersrequirements | |||||
PACKING | appr. 1mtbig-bag |
Ferro phosphorus is used mainly as the additives in the foundry industry to improve the floatability of foundry iron, thus improving the quality of the castings. Phosphorus content can increase the wearing resistance and improve the cutability in the castings. Ferro phosphorus also used as the additive in the steel production, which can improve the corrosion resistivity in certain steel products.
P | Si | C | S | Cu | V | |
FeP | 23-28 % | 1-2 % | 0.1 % max | 0.01 % max | 0.5 % max | 0.5 % max |
SIZE | 10-50 mm / 10-100 mm | |||||
PACKING | 1 mt big-bag |
Hot Briquetted Iron (HBI) is a premium form of Direct Reduced Iron (DRI)* that has been compacted at a temperature greater than 650° C at time of compaction and has a density greater than 5000 kilograms per cubic meter (5000 kg/m3).
*DRI is a metallic material produced from iron oxide fines or iron oxide pellets and/or lump ores that have been reduced (oxygen removed) without reaching the melting point of iron.
Listed by IMO as: Direct Reduced Iron (A) Briquettes, hot-moulded
International Maritime Solid Bulk Cargoes (IMSBC) Code, which on 1 January 2011 supersedes the Code of Safe Practice for Solid Bulk Cargoes (BC Code), 1994 Edition Description of HBI:
HBI is a premium quality, high density steel industry raw material containing 90-94% total iron (Fe) in a nearly pure form, which is used in Electric Arc Furnace (EAF) and Basic Oxygen Furnace (BOF) steelmaking, Blast Furnace (BF) ironmaking, and foundry applications.